Etching and forward transfer of fused silica in solid-phase by femtosecond laser-induced solid etching (LISE)

Etching and forward transfer of fused silica in solid-phase by femtosecond laser-induced solid etching (LISE)
Etching and forward transfer of fused silica in solid-phase by femtosecond laser-induced solid etching (LISE)
We present a novel, laser-based microstructuring technique for the etching and deposition of solid materials. This technique, which we call laser-induced solid etching (LISE), utilises the absorption of femtosecond duration laser pulses in a constrained metal film between two bulk substrates, at least one of which is transparent to the laser wavelength. The very rapid pressure increase in the metal film following irradiation is believed to initiate crack-propagation in one or other of the bulk substrates. By spatially shaping the laser beam, the cracking process can be controlled to etch solid chunks of material from the substrates. Using LISE we have etched smooth, micron-scale pits and trenches in silicon and silica. The results will be compared to etched features produced using conventional techniques. A unique feature of LISE is that the material etched from the bulk substrate is removed as a single solid piece and is not shattered, melted, or vaporised by the process. Hence, the etched material can be collected on the other bulk substrate used in the process. In this way, we have deposited micron-scale dots and lines of silica onto silicon and vice-versa. The deposited structures obtained using LISE compare well with those obtained with conventional laser forward transfer techniques. Minimal evidence of melting during the process has been observed, suggesting that LISE may be a useful technique for the forward transfer direct-write of intact solid materials
0169-4332
8343-8351
Banks, David P.
293424e9-92eb-46f3-8871-40e8d3672b3c
Kaur, Kamal S.
aedd9bea-c39d-41c8-9ae3-845cda3b4ff7
Eason, Robert W.
e38684c3-d18c-41b9-a4aa-def67283b020
Banks, David P.
293424e9-92eb-46f3-8871-40e8d3672b3c
Kaur, Kamal S.
aedd9bea-c39d-41c8-9ae3-845cda3b4ff7
Eason, Robert W.
e38684c3-d18c-41b9-a4aa-def67283b020

Banks, David P., Kaur, Kamal S. and Eason, Robert W. (2009) Etching and forward transfer of fused silica in solid-phase by femtosecond laser-induced solid etching (LISE). Applied Surface Science, 255 (20), 8343-8351. (doi:10.1016/j.apsusc.2009.05.060).

Record type: Article

Abstract

We present a novel, laser-based microstructuring technique for the etching and deposition of solid materials. This technique, which we call laser-induced solid etching (LISE), utilises the absorption of femtosecond duration laser pulses in a constrained metal film between two bulk substrates, at least one of which is transparent to the laser wavelength. The very rapid pressure increase in the metal film following irradiation is believed to initiate crack-propagation in one or other of the bulk substrates. By spatially shaping the laser beam, the cracking process can be controlled to etch solid chunks of material from the substrates. Using LISE we have etched smooth, micron-scale pits and trenches in silicon and silica. The results will be compared to etched features produced using conventional techniques. A unique feature of LISE is that the material etched from the bulk substrate is removed as a single solid piece and is not shattered, melted, or vaporised by the process. Hence, the etched material can be collected on the other bulk substrate used in the process. In this way, we have deposited micron-scale dots and lines of silica onto silicon and vice-versa. The deposited structures obtained using LISE compare well with those obtained with conventional laser forward transfer techniques. Minimal evidence of melting during the process has been observed, suggesting that LISE may be a useful technique for the forward transfer direct-write of intact solid materials

Text
4379.pdf - Accepted Manuscript
Download (2MB)

More information

Published date: 30 July 2009

Identifiers

Local EPrints ID: 78904
URI: http://eprints.soton.ac.uk/id/eprint/78904
ISSN: 0169-4332
PURE UUID: 4b919ac8-a0b5-40c7-9723-a82e0c43e2da
ORCID for Robert W. Eason: ORCID iD orcid.org/0000-0001-9704-2204

Catalogue record

Date deposited: 15 Mar 2010
Last modified: 14 Mar 2024 02:33

Export record

Altmetrics

Contributors

Author: David P. Banks
Author: Kamal S. Kaur
Author: Robert W. Eason ORCID iD

Download statistics

Downloads from ePrints over the past year. Other digital versions may also be available to download e.g. from the publisher's website.

View more statistics

Atom RSS 1.0 RSS 2.0

Contact ePrints Soton: eprints@soton.ac.uk

ePrints Soton supports OAI 2.0 with a base URL of http://eprints.soton.ac.uk/cgi/oai2

This repository has been built using EPrints software, developed at the University of Southampton, but available to everyone to use.

We use cookies to ensure that we give you the best experience on our website. If you continue without changing your settings, we will assume that you are happy to receive cookies on the University of Southampton website.

×