Fabrication of high numerical aperture fluoroaluminate fibres

Fabrication of high numerical aperture fluoroaluminate fibres
Fabrication of high numerical aperture fluoroaluminate fibres
A family of fluoroaluminate glasses has been identified as the ideal host for doping with Nd3+ for use in the development of lasers and amplifiers in the second telecom window. For optimum performance, a fibre with high numerical aperture (NA), fibre length of 5cm and loss of 10dB/m is required. The high NA implies a core diameter of 3µm is needed and thus the core-to-clad interface represents greater than 50% of the core area. Crystallisation in the interface introduces large scattering losses. The critical step in the fabrication process is preform fabrication. We will present results comparing the different techniques employed and thermal and mechanical fabrication process modelling consistent with our experimental observations and detail the advantages and limiting parameters for the different processes. Rod-in-tube is the simplest technique of preform fabrication and works exceptionally well for oxide glasses. Fluorides are highly prone to surface crystallisation. We have looked at the fibre losses as functions of polishing material, polishing time, and etching. It is a good first step to test the optical properties and performance in a fibre.
Rotational casting is usually employed in fluoride glasses. The high Tg(450°C) and large expansion coefficient ( >150x10-7/°K. We will compare the results of rotational casting with built-in-casting and the influence of processing time, thermal history and mould material (thermal conductivity).
Extrusion as a procedure for preform fabrication is specially suitable for fluoraluminates. Extrusion allows one to operate at temperatures nearer Tg than Tx. Preforms can be prepared with small cores and thus avoid the thermal cycling involved in sleeving to get the singlemode fibre. To date our losses for fibres with 5-8µm cores vary from 100dB/m using rod-in-tube to 20dB/m using extrusion.
Taylor, E.R.
d9a73a87-6abd-4a1e-a462-84549c667d19
Moore, R.C.
a7d68363-4127-4f7b-9da4-ef66d19ab327
Tucknott, J.A.
e5030b83-5077-498c-821f-af0b3b68fb10
Harwood, D.W.J.
1103aa43-a21d-41a1-aa9c-d180fb4ef95d
West, Y.
22123bfa-175b-4da9-8b07-d860bfaf9bb4
Payne, D.N.
4f592b24-707f-456e-b2c6-8a6f750e296d
Taylor, E.R.
d9a73a87-6abd-4a1e-a462-84549c667d19
Moore, R.C.
a7d68363-4127-4f7b-9da4-ef66d19ab327
Tucknott, J.A.
e5030b83-5077-498c-821f-af0b3b68fb10
Harwood, D.W.J.
1103aa43-a21d-41a1-aa9c-d180fb4ef95d
West, Y.
22123bfa-175b-4da9-8b07-d860bfaf9bb4
Payne, D.N.
4f592b24-707f-456e-b2c6-8a6f750e296d

Taylor, E.R., Moore, R.C., Tucknott, J.A., Harwood, D.W.J., West, Y. and Payne, D.N. (1998) Fabrication of high numerical aperture fluoroaluminate fibres. XI International Symposium on Non-Oxide Glasses and New Optical Glasses, Sheffield, United Kingdom. 06 - 10 Sep 1998.

Record type: Conference or Workshop Item (Paper)

Abstract

A family of fluoroaluminate glasses has been identified as the ideal host for doping with Nd3+ for use in the development of lasers and amplifiers in the second telecom window. For optimum performance, a fibre with high numerical aperture (NA), fibre length of 5cm and loss of 10dB/m is required. The high NA implies a core diameter of 3µm is needed and thus the core-to-clad interface represents greater than 50% of the core area. Crystallisation in the interface introduces large scattering losses. The critical step in the fabrication process is preform fabrication. We will present results comparing the different techniques employed and thermal and mechanical fabrication process modelling consistent with our experimental observations and detail the advantages and limiting parameters for the different processes. Rod-in-tube is the simplest technique of preform fabrication and works exceptionally well for oxide glasses. Fluorides are highly prone to surface crystallisation. We have looked at the fibre losses as functions of polishing material, polishing time, and etching. It is a good first step to test the optical properties and performance in a fibre.
Rotational casting is usually employed in fluoride glasses. The high Tg(450°C) and large expansion coefficient ( >150x10-7/°K. We will compare the results of rotational casting with built-in-casting and the influence of processing time, thermal history and mould material (thermal conductivity).
Extrusion as a procedure for preform fabrication is specially suitable for fluoraluminates. Extrusion allows one to operate at temperatures nearer Tg than Tx. Preforms can be prepared with small cores and thus avoid the thermal cycling involved in sleeving to get the singlemode fibre. To date our losses for fibres with 5-8µm cores vary from 100dB/m using rod-in-tube to 20dB/m using extrusion.

Text
1621 - Author's Original
Download (178kB)

More information

Published date: 1998
Venue - Dates: XI International Symposium on Non-Oxide Glasses and New Optical Glasses, Sheffield, United Kingdom, 1998-09-06 - 1998-09-10

Identifiers

Local EPrints ID: 76654
URI: http://eprints.soton.ac.uk/id/eprint/76654
PURE UUID: 61c51070-9ad8-472e-9a26-5fcd87318418

Catalogue record

Date deposited: 11 Mar 2010
Last modified: 13 Mar 2024 23:25

Export record

Contributors

Author: E.R. Taylor
Author: R.C. Moore
Author: J.A. Tucknott
Author: D.W.J. Harwood
Author: Y. West
Author: D.N. Payne

Download statistics

Downloads from ePrints over the past year. Other digital versions may also be available to download e.g. from the publisher's website.

View more statistics

Atom RSS 1.0 RSS 2.0

Contact ePrints Soton: eprints@soton.ac.uk

ePrints Soton supports OAI 2.0 with a base URL of http://eprints.soton.ac.uk/cgi/oai2

This repository has been built using EPrints software, developed at the University of Southampton, but available to everyone to use.

We use cookies to ensure that we give you the best experience on our website. If you continue without changing your settings, we will assume that you are happy to receive cookies on the University of Southampton website.

×